Virgin Rotomoulding Powder
Viasola is one of the leading manufacturer, supplier & exporter of Virgin Rotomoulding Powder.
The break obstruction ought to be a significant thought while choosing a grade of polyethylene for a specific application. When exposed to worry about a timeframe most materials normally fizzle by breaking. Comprehend that various grades of Polyethylene can display limitlessly unique execution regarding break obstruction.
The break opposition of a particular grade of Linear Low-Density Polyethylene is represented generally by the size of its atoms (demonstrated by its Melt Index) and the sort and level of comonomer utilized in its production. Comonomers like butene (C4), hexene (C6) and octene (C8) are responded into the polymer affix to deliver little side chains which thus make a deviation, or change of point in the atom chain.
Virgin PLASTIC GRANULES
LDPE Virgin Plastic Granules is widely used for manufacturing various containers, dispensing bottles, wash bottles, tubing, plastic bags for computer components, and various molded laboratory equipment. Its most common use is in plastic bags. At Roto Polymers we use the state-of-the-art manufacturing to produce LDPE Reprocessed Plastic Granules as per customers’ requirements and standards. Highest quality standards and timely delivery schedules give us an edge over our competitors.
- High Flame Resistance
- Non-Oxidising Character
- Durability
Grades Detail
Grading of GreenEthene powders is based on density, melt flow, impact resistance, rigidity, ESCR (Environmental Stress Crack Resistance), grind type and custom compound colors.
| Butene Grades Specifications | Grade Name | |||||
|---|---|---|---|---|---|---|
| RotoThene5GUV | RotoThene5NG | |||||
| Specimen Type | ||||||
| Parameter | Standard | UOM | Compression Molded | Rotomolded | Compression Molded | Rotomolded |
| MFI | ASTM D1238 | gm/10 min | 4.5 | 3.8 | ||
| Density | ASTM D 1505 | gm/cm³ | 0.936 | 0.939 | ||
| Recommended PIAT * | In-lab StdPrc * | °C | 190 °C | 190 °C | ||
| Tensile Strength at Yield | ASTM D638 | (kg/cm²) (MPa) (Psi) | (180) (17.5) (2540) | (185) (18) (2610) | (215) (21) (3050) | (210) (20.5) (2975) |
| Tensile Strength at Break | ASTM D638 | (kg/cm²) (MPa) (Psi) | – | (120) (11.75) (1705) | – | (120) (11.75) (1705) |
| IZOD Impact Strength | ASTM D256 | Kg.cm/cm | 25 | – | 22 | – |
| ARM Low Temperature | ARM Standard (3.17mm @ -40 °C/°F) | (J/mm) (ft/lbs) | – | (22) (80) | – | (22) (80) |
| Flexural Modulus At 1% Strain | ASTM D790 | (kg/cm²) (MPa) (Psi) | (6000) (590) (85575) | (2300) (225) (32630) | (9000) (880) (127625) | (2300) (225) (32630) |
| Elongation at Yield | ASTM D638 | % | 20 | 14 | 15 | 12 |
| Elongation at Break | ASTM D638 | % | 600 | 165 | 350 | 110 |
| ESCR | ASTM D1693 | Hrs | 350 | 350 | 300 | 300 |
*PIAT “ For moulding oven temperature was 300 oC and cube mould of size 175mmx175mmx175mm was moulded with wall thickness of 3.17mm.
Application Industries
Grading of GreenEthene powders is based on density, melt flow, impact resistance, rigidity, ESCR (Environmental Stress Crack Resistance), grind type and custom compound colors.